Indflydelsen af mikrosilicas egenskaber på højkvalitetsbetons reologi

Abstract

Denne rapport beskæftiger sig med undersøgelser af mikrosilicas egenskaber på High Performance Concrete (HPC), hvor formålet er at optimere brugen af dette materiale, således at en tættere og stærkere beton opnås. Det findes ud fra teoretiske pakningsberegninger, at det bedste forhold mellem cement og mikrosilica er 80%/20%. Ved brug af dette forhold opnås den højeste pakningsgrad, og derved også den største tæthed. Derefter undersøges brugen af disse materialer i forsøg udført på mørtler. Fors øgene handler både om de reologiske egenskaber for HPC samt styrker og tæthed ved brug af forskellige typer cement, mikrosilica og superplastificerende tilsætningsstoffer(SPT). Resultaterne viser, at SPT-typen Betanaphtalensulfornat (BNS) ikke virker sammen med rapid cement, og at SPT-typen Polycarboxyleter (PCE) med lange sidekæder og stærk ladning ikke virker i en HPC-mørtel. Derudover er det fundet, at mikrosilicas specifikke overflade er afgørende for HPC's støbelighed. Dette er dokumenteret ved sammenligning af tre forskellige mikrosilicaer med forskellige specifikke overflader. Desuden er trykstyrken fundet for de bedste HPC-mørtler, og en syvdøgns styrke på 100MPa er opnået. Til sidst er kapillarsugningsevnen for mørtlerne undersøgt, og her er et kapillaritetstal på 0,11 g/m2 s½ fundet.

This report deals with the study of silica fumes proporties in High Performance Concrete (HPC), where the objective is to optimize the use of this material so that a more compact and stronger concrete is created. It is derived from theoretical calculations that the best ratio between cement and silica fume is 80%/20%. By using this ratio the highest degree of packing is achieved and thereby a more compact concrete is achieved. Subsequently these materials are used in experiments performed on morters. The experiments are about the rheological properties, strenght and sorptivity of HPC-morters by the use of different types of cement, silica fumes and high range water reducers. The results show that the high range water reducer Betanaphtalensulfornat (BNS) and rapid cement do not work together and the high range water reducer Polycarboxyleter (PCE) with long side chains and high strength do not work in a HPC-morter. It is also found that silica fume's specific surface is crucial for HPC's casting abillity. This is documented by comparison of three different silica fumes with different specific surfaces. Moreover the strength is found for the best HPC-morters and a result of 100MPa after hardning in seven days is obtained. Finally a sorptivitytest is performed and the results show a sorptivity of 0,11 g/m2 s½ as the lowest.

Kolofon: Denne side er en del af AAU Studenterprojekter — Aalborg Universitets studenterprojektportal. Her kan du finde og downloade offentligt tilgængelige kandidatspecialer og masterprojekter fra hele universitetet fra 2008 og frem. Studenterprojekter fra før 2008 kan findes i trykt form på Aalborg Universitetsbibliotek.

Har du spørgsmål til AAU Studenterprojekter eller Aalborg Universitets forskningsregistrering, formidling og analyse, er du altid velkommen til at kontakte VBN-teamet. Du kan også læse mere i AAU Studenterprojekter FAQ.

A master thesis from Aalborg University

Indflydelsen af mikrosilicas egenskaber på højkvalitetsbetons reologi

[The influence of silica fumes properties on the rheology of High Performance Concrete]