Regulering af selvkompakterende betons reologi ved tilsætning af lermineraler
Oversat titel
Adjustment of the rheology of self compacting concrete by addition of clay minerals
Forfattere
Pilegaard Madsen, Thomas ; Beier Jensen, Henrik ; Bjerre Ruggaard, Christian
Semester
4. semester
Uddannelse
Udgivelsesår
2009
Antal sider
240
Abstract
Projektet undersøger, om tilsætning af lermineraler kan reducere risikoen for separation i frisk beton (at grovere partikler synker, mens vand/pasta skilles). Der blev brugt et lokalt lerslam fra afvaskning af tilslagsmaterialer og et kommercielt lerprodukt. Forsøgene viste, at begge lerprodukter stabiliserer betonen. Stabiliteten blev vurderet via følsomheden af flydemålet (hvor meget den friske beton flyder ud) og via risikoen for separation ved ændringer i vandindholdet. Tilsætning af ler kræver øget pastavolumen for at opnå de ønskede reologiske egenskaber (flydeevne og sammenhæng). En laseranalyse viste, at begge lerprodukters kornkurver minder om flyveaske. Derfor blev ler erstattet med tilsvarende mængder flyveaske i forsøg; dette viste, at stabiliteten ikke skyldes partikelstørrelse, men lerpartiklernes form og evne til at optage vand. Målinger af trykstyrke og elasticitetskoefficient på hærdede prøvelegemer viste ingen væsentlig påvirkning af disse egenskaber ved lertilsætning.
This project investigates whether adding clay minerals can reduce the risk of segregation in fresh concrete (coarse particles settling while water/paste separate). A locally sourced clay slurry from washing aggregates and a commercial clay product were used. Experiments showed that both clay products stabilize the concrete. Stability was assessed by the sensitivity of the slump flow (how far fresh concrete spreads) and the risk of segregation under changes in water content. Adding clay requires an increased paste volume to achieve the desired rheological properties (flowability and cohesion). A laser analysis showed that both clay products have particle size distributions similar to fly ash. Based on this, clay was replaced with equivalent amounts of fly ash in tests; results showed that stability is not due to particle size, but to the clay minerals’ particle shape and ability to absorb water. Measurements on hardened specimens indicated that compressive strength and modulus of elasticity are not significantly affected by adding clay.
[Dette resumé er genereret ved hjælp af AI]
Emneord
Ler ; mineraler ; selvkompakterende beton ; stabilisering ; reologi ; separation ; lermineraler ; flydemål ; dickit ; kaolin ; tilslag ; vandindhold ; clay ; minerals ; self compacting concrete ; stabilizing ; rheology ; segregation ; clay minerals ; slump flow ; dickite ; kaolinite ; aggregates ; water content